The perlite separates the heat preservation board (FSG hatred water heat preservation board) is take the inflated pearlite bulk as an aggregate, joins the water-repellent and the cementing agent carries on the heat insulation waterproofing heat preservation board which working procedures and so on configuration, screening, compression formation, drying make. The FSG hatred water heat preservation board has solved each kind of building roofing heat preservation, the heat insulation and the waterproof function effectively in a body's technical difficult problem, saved the massive constructions and the service fund.product characteristic:The nature is light, and heat preservation heat insulation performance fine fire protection. Dustproof. Moisture-proof, does not distort the modification, not rottenly mildewy, the non-toxic tasteless hatred water performance to be good, hates Shui Lvke to reach above 98% to construct safely easy and feasible, the roofing and the wall surface glue may the natural ore be raw materials, has the good environment-protective.珍珠巖保溫板（FSG憎水保溫板）是以膨脹珍珠巖散料為骨料，加入防水劑和粘結劑進行配制、篩選、加壓成型、烘干等工序制成的隔熱防水保溫板。FSG憎水保溫板有效地解決了各類建筑屋面保溫、隔熱和防水功能于一體的技術難題，節約了大量的建設和維修資金。 

    憎水珍珠巖保溫板產品特點： [中信珍珠巖]

    憎水珍珠巖保溫板質輕且保溫隔熱性能優良防火.防塵.防潮,不變形改性、不腐爛發霉、無毒無味憎水性能好，憎水率可達98％以上施工安全簡單易行,屋面與墻面粘貼均可天然礦石為原料,有良好的環保性.【中信珍珠巖-冷小林】
    憎水珍珠巖保溫板主要用于住宅、工業、公共建筑的墻體及樓房屋面、游泳池、冷庫、鍋爐及一些防水等特殊要求的保溫工程。【中信珍珠巖-冷小林】

    憎水珍珠巖保溫板主要技術指標：[中信珍珠巖]

性   能	單     位	指     標
密度	kg/m3	≤250
導熱系數	w/m.k	≤0.076
重量含水率	%	≤5
抗壓程度	Kpa	≥474
憎水率	%	99.2
使用溫度范圍	℃	－40－600

    憎水珍珠巖保溫板性能指標：[中信珍珠巖]

檢驗項目	標準要求	檢驗結果
抗壓密度	≥294	299
長度（mm）	500+/-2	303
寬度（mm）	300+/-2	402
厚度（mm）	(30-150)+/-2	99
重量含水率（％）	≤5	5
對角線	≤10	7

  

Product Readme

The perlite separates the heat preservation board (FSG hatred water heat preservation board) is take the inflated pearlite bulk as an aggregate, joins the water-repellent and the cementing agent carries on the heat insulation waterproofing heat preservation board which working procedures and so on configuration, screening, compression formation, drying make. The FSG hatred water heat preservation board has solved each kind of building roofing heat preservation, the heat insulation and the waterproof function effectively in a body's technical difficult problem, saved the massive constructions and the service fund. product characteristic: The nature is light, and heat preservation heat insulation performance fine fire protection. Dustproof. Moisture-proof, does not distort the modification, not rottenly mildewy, the non-toxic tasteless hatred water performance to be good, hates Shui Lvke to reach above 98% to construct safely easy and feasible, the roofing and the wall surface glue may the natural ore be raw materials, has the good environment-protective.   Item Comparison 200號 250號 350號 Excellent Regular Excellent Regular Regular LBD ≤200 ≤250 ≤350 Anti-stress intensity ≥0.40 ≥0.30 ≥0.50 ≥0.40 ≥0.40 Anti-break intensity ≥0.20 _____ ≥0.25 ______ _____ Heat conductiving ≤0.060 ≤0.068 ≤0.068 ≤0.072 ≤0.087 Moisture rate ≤2 ≤5 ≤2 ≤5 ≤10 Waterptoof Ratio ＞98       歡迎來電咨詢，真誠合作。

以氣凝膠膨脹珍珠巖為骨料,P·O 42.5級水泥和熟石膏的混合物為膠結材料,添加可再分散性乳膠粉、羥丙基甲基纖維素制備保溫板。使用單因素法分析了硅酸鹽水泥和熟石膏的配料及抗壓強度的關系;采用正交試驗法研究了配料用量和保溫板抗壓強度、導熱系數的關系。制得保溫板的導熱系數低至0.045 W/(m·K),抗壓強度達到0.54 MPa。試驗采用X射線衍射分析了膠結材料的反應,使用紅外光譜技術研究了氣凝膠膨脹珍珠巖的疏水特性。 以導熱系數極低的物質氣凝膠為研究對象,使其與膨脹珍珠巖復合,制成氣凝膠膨脹珍珠巖。對比級配與非級配氣凝膠膨脹珍珠巖膠凝材料的傳熱性能,建立數值模型模擬氣凝膠膨脹珍珠巖的粒徑級配在傳熱中的作用,推導出氣凝膠膨脹珍珠巖膠凝材料的傳熱規律。根據氣凝膠膨脹珍珠巖的特性研制建筑保溫材料,測試這種新型保溫材料的導熱系數和力學性能。計算太原地區氣象參數下氣凝膠膨脹珍珠巖保溫材料圍護建筑的年制熱制冷能耗值為57.45 kWh/m2,與普通圍護建筑109.90kWh/m2相比,實現能耗的大幅降低。本文研究的具體內容如下:(1)使用不同硅源、酸堿催化劑和改性置換劑研制低導熱氣凝膠。

尹太銀生產的乳化瀝青珍珠巖是一種以乳化瀝青為膠結劑，與膨脹珍珠巖砂混合，在常溫下經攪拌加壓成型的新型保溫材料。它具有容重輕、保溫性能好、吸濕率低、冷作業施工易于保證質量等優點。它用作屋面保溫層，既可現澆又可預制。乳化瀝青膨脹珍珠巖主要用于異性設備、罐體，球體墻壁的保溫和隔音，具有施工方便，易操作。本產品不腐蝕設備，且無放射性，符合國家環保要求，是其它傳統保溫產品無法比擬的換代高效節能新材料。它是以瀝青為粘結劑的膨脹珍珠巖絕熱保溫板，包括石油瀝青膨脹珍珠巖保溫板和乳化瀝青膨脹珍珠巖保溫板兩種類型。膨脹珍珠巖的密度要求小于120 kg/m3。

FSG憎水樹脂膨脹珍珠巖保溫板屋面保溫隔熱操作工藝1、工藝流程基層清理─→彈線找坡─→管根固定─→隔汽層鋪設─→抹找平層。2、操作步1）先將接觸面清掃干凈。2）按設計坡度及流水方向，找出屋面坡度走向，確定FSG憎水樹脂膨脹珍珠巖保溫板保溫層的厚度范圍。（3）穿越結構層的管根在FSG憎水樹脂膨脹珍珠巖保溫板保溫層施工前，應用細石砼塞堵密實。（4）FSG憎水樹脂膨脹珍珠巖保溫板應緊靠在需保溫的基層表面上并應鋪平墊穩，分層鋪設的板材，其上、下兩層的接縫應錯開，板之間用膠水貼嚴、粘牢，各層板間的縫隙，應用同類材料的碎屑嵌填密實，表面應與相鄰兩板的高度一致排汽槽的留置應與砂漿找平層分格縫一致，做找平層之前用寬約6cm的鍍鋅鐵皮覆蓋排汽道之上，以免水泥砂漿堵塞。